When did they start threading glass bottles?

08 Apr.,2024

 

Roman cage cup from the 4th century CE

The history of glass-making dates back to at least 3,600 years ago in Mesopotamia. However, most writers claim that they may have been producing copies of glass objects from Egypt.[1] Other archaeological evidence suggests that the first true glass was made in coastal north Syria, Mesopotamia or Egypt.[2] The earliest known glass objects, of the mid 2,000 BCE, were beads, perhaps initially created as the accidental by-products of metal-working (slags) or during the production of faience, a pre-glass vitreous material made by a process similar to glazing.[n 1] Glass products remained a luxury until the disasters that overtook the late Bronze Age civilizations seemingly brought glass-making to a halt.

Development of glass technology in India may have begun in 1,730 BCE.[3]

From across the former Roman Empire, archaeologists have recovered glass objects that were used in domestic, industrial and funerary contexts. Anglo-Saxon glass has been found across England during archaeological excavations of both settlement and cemetery sites. Glass in the Anglo-Saxon period was used in the manufacture of a range of objects, including vessels, beads, windows, and was even used in jewellery.

Origins

[

edit

]

Naturally occurring glass, especially the volcanic glass obsidian, has been used by many Stone Age societies across the globe for the production of sharp cutting tools and, due to its limited source areas, was extensively traded. But in general, archaeological evidence suggests that the first true glass was made in coastal north Syria, Mesopotamia or ancient Egypt.[2] Because of Egypt's favorable environment for preservation, the majority of well-studied early glass is found there, although some of this is likely to have been imported. The earliest known glass objects, of the mid-third millennium BCE, were beads, perhaps initially created as accidental by-products of metal-working (slags) or during the production of faience, a pre-glass vitreous material made by a process similar to glazing.[n 1]

During the Late Bronze Age in Egypt (e.g., the Ahhotep "Treasure")[4] and Western Asia (e.g., Megiddo),[5] there was a rapid growth in glassmaking technology. Archaeological finds from this period include colored glass ingots, vessels (often colored and shaped in imitation of highly prized hardstone carvings in semi-precious stones) and the ubiquitous beads. The alkali of Syrian and Egyptian glass was soda ash (sodium carbonate), which can be extracted from the ashes of many plants, notably halophile seashore plants like saltwort. The latest vessels were 'core-formed', produced by winding a ductile rope of glass around a shaped core of sand and clay over a metal rod, then fusing it by reheating it several times.[citation needed]

Threads of thin glass of different colors made with admixtures of oxides were subsequently wound around these to create patterns, which could be drawn into festoons by using metal raking tools. The vessel would then be rolled smooth (marvered) on a slab in order to press the decorative threads into its body. Handles and feet were applied separately. The rod was subsequently allowed to cool as the glass slowly annealed and was eventually removed from the center of the vessel, after which the core material was scraped out. Glass shapes for inlays were also often created in moulds. Much of early glass production, however, relied on grinding techniques borrowed from stone working. This meant that the glass was ground and carved in a cold state.[6]

By the 15th century BCE, extensive glass production was occurring in Western Asia, Crete, and Egypt; and the Mycenaean Greek term 𐀓𐀷𐀜𐀺𐀒𐀂, ku-wa-no-wo-ko-i, meaning "workers of lapis lazuli and glass" (written in Linear b syllabic script) is attested.[7][8][9][n 2][n 3] It is thought that the techniques and recipes required for the initial fusing of glass from raw materials were a closely guarded technological secret reserved for the large palace industries of powerful states. Glass workers in other areas therefore relied on imports of preformed glass, often in the form of cast ingots such as those found on the Ulu Burun shipwreck off the coast of modern Turkey.[citation needed]

An early 18th-century goblet with coats of arms in the District Museum in Tarnów is one of the highest (54.3 cm, 21.4 in) preserved examples of artistry of less known Lubaczów glass manufacturing factory.[12] The goblet was almost entirely covered with a pattern of so-called carp scales and hand-engraved decoration.[12]

Glass remained a luxury material, and the disasters that overtook Late Bronze Age civilizations seemed to have brought glass-making to a halt.[citation needed] It picked up again in its former sites, Syria and Cyprus, in the 9th century BCE, when the techniques for making colorless glass were discovered.[citation needed]

The first glassmaking "manual" dates back to ca. 650 BCE. Instructions on how to make glass are contained in cuneiform tablets discovered in the library of the Assyrian king Ashurbanipal.[citation needed]

In Egypt, glass-making did not revive until it was reintroduced in Ptolemaic Alexandria. Core-formed vessels and beads were still widely produced, but other techniques came to the fore with experimentation and technological advancements.[citation needed]

During the Hellenistic period many new techniques of glass production were introduced and glass began to be used to make larger pieces, notably table wares. Techniques developed during this period include 'slumping' viscous (but not fully molten) glass over a mould in order to form a dish and 'millefiori' (meaning 'thousand flowers') technique, where canes of multicolored glass were sliced and the slices arranged together and fused in a mould to create a mosaic-like effect. It was also during this period that colorless or decolored glass began to be prized and methods for achieving this effect were investigated more fully.[13]

According to Pliny the Elder, Phoenician traders were the first to stumble upon glass manufacturing techniques at the site of the Belus River. Georgius Agricola, in De re metallica, reported a traditional serendipitous "discovery" tale of familiar type:

"The tradition is that a merchant ship laden with nitrum being moored at this place, the merchants were preparing their meal on the beach, and not having stones to prop up their pots, they used lumps of nitrum from the ship, which fused and mixed with the sands of the shore, and there flowed streams of a new translucent liquid, and thus was the origin of glass."[14]

This account is more a reflection of Roman experience of glass production, however, as white silica sand from this area was used in the production of glass within the Roman Empire due to its high purity levels. During the 1st century BCE, glass blowing was discovered on the Syro-Judean coast, revolutionizing the industry. The first evidence of the invention of glassblowing was found in the Jewish Quarter of Jerusalem, in a layer of fill inside a ritual bath that was overlain with the paving stones of the Herodian street.[15] Several other site of producing "Judean Glass" were found in Galilee.[16] Glass vessels were now inexpensive compared to pottery vessels. Growth of the use of glass products occurred throughout the Roman world.[citation needed] Glass became the Roman plastic, and glass containers produced in Alexandria[citation needed] spread throughout the Roman Empire. With the discovery of clear glass (through the introduction of manganese dioxide), by glass blowers in Alexandria circa 100 AD, the Romans began to use glass for architectural purposes. Cast glass windows, albeit with poor optical qualities, began to appear in the most important buildings in Rome and the most luxurious villas of Herculaneum and Pompeii. Over the next 1,000 years, glass making and working continued and spread through southern Europe and beyond.[citation needed]

History by culture

[

edit

]

Iran

[

edit

]

The first Persian glass comes in the form of beads dating to the late Bronze Age (1600 BCE), and was discovered during the explorations of Dinkhah Tepe in Iranian Azerbaijan by Charles Burney. Glass tubes were discovered by French archaeologists at Chogha Zanbil, belonging to the middle Elamite period. Mosaic glass cups have also been found at Teppe Hasanlu and Marlik Tepe in northern Iran, dating to the Iron Age. These cups resemble ones from Mesopotamia, as do cups found in Susa during the late Elamite period.

Glass tubes containing kohl have also been found in Iranian Azerbaijan and Kurdistan Province, belonging to the Achaemenid period. During this time, glass vessels were usually plain and colorless. By the Seleucid and late Parthian era, Greek and Roman techniques were prevalent. During the Sasanian period, glass vessels were decorated with local motifs.[17]

India

[

edit

]

Evidence of glass during the chalcolithic has been found in Hastinapur, India.[18] The earliest glass item from the Indus Valley civilization is a brown glass bead found at Harappa, dating to 1700 BCE. This makes it the earliest evidence of glass in South Asia.[3][19] Glass discovered from later sites dating from 600 to 300 BCE displays common colors.[3]

Texts such as the Shatapatha Brahmana and Vinaya Pitaka mention glass, implying they could have been known in India during the early first millennium BCE.[18] Glass objects have also been found at Beed, Sirkap and Sirsukh, all dating to around the 5th century BCE.[20] However, the first unmistakable evidence for widespread glass usage comes from the ruins of Taxila (3rd century BCE), where bangles, beads, small vessels, and tiles were discovered in large quantities.[18] These glassmaking techniques may have been transmitted from cultures in Western Asia.[20]

The site of Kopia, in Uttar Pradesh, is the first site in India to locally manufacture glass, with items dating between the 7th century BCE to the 2nd century CE.[21] Early Indian glass of this period was likely made locally, as they differ significantly in chemical composition when compared to Babylonian, Roman and Chinese glass.[20]

By the 1st century AD, glass was being used for ornaments and casing in South Asia.[18] Contact with the Greco-Roman world added newer techniques, and Indians artisans mastered several techniques of glass molding, decorating and coloring by the succeeding centuries.[18] The Satavahana period of India also produced short cylinders of composite glass, including those displaying a lemon yellow matrix covered with green glass.[22]

China

[

edit

]

Xianbei glass water dropper Blue glass plaques found in the Mausoleum of the Nanyue King, dating from late 2nd century BCE

In China, glass played a peripheral role in arts and crafts when compared to ceramics and metal work.[23] The earliest glass items in China come from the Warring States period (475–221 BCE), although they are rare in number and limited in archaeological distribution.

Glassmaking developed later in China compared to cultures in Mesopotamia, Egypt and India.[24] Imported glass objects first reached China during the late Spring and Autumn period (early 5th century BCE), in the form of polychrome eye beads.[25] These imports created the impetus for the production of indigenous glass beads.

During the Han Dynasty (206 BCE–220 CE), the use of glass diversified. The introduction of glass casting in this period encouraged the production of moulded objects, such as bi disks and other ritual objects.[24] Chinese glass objects from the Warring States and Han period vary greatly in chemical composition from the imported glass objects. The glasses from this period contain high levels of barium oxide and lead, distinguishing them from the soda–lime–silica glasses of Western Asia and Mesopotamia.[26] At the end of the Han Dynasty (AD 220), the lead-barium glass tradition declined, with glass production only resuming during the 4th and 5th centuries AD.[27] Literary sources also mention the manufacture of glass during the 5th century AD.[28]

Romans

[

edit

]

Roman glass

Roman glass production developed from Hellenistic technical traditions, initially concentrating on the production of intensely colored, cast glass vessels. Glass objects have been recovered across the Roman Empire[29] in domestic, funerary[30] and industrial contexts.[31] Glass was used primarily for the production of vessels, although mosaic tiles and window glass were also produced.

However, during the 1st century AD, the industry underwent rapid technical growth that saw the introduction of glass-blowing and the dominance of colorless or ‘aqua’ glasses. Raw glass was produced in geographically separate locations to the working of glass into finished vessels,[32][33] and, by the end of the 1st century CE, large scale manufacturing, primarily in Alexandria,[34] resulted in the establishment of glass as a commonly available material in the Roman world.

Islamic world

[

edit

]

Islamic glass continued the achievements of pre-Islamic cultures, especially the Sasanian glass of Persia. The Arab poet al-Buhturi (820–897) described the clarity of such glass: "Its color hides the glass as if it is standing in it without a container."[35] In the 8th century, the Persian-Arab chemist Jābir ibn Hayyān (Geber) described 46 recipes for producing colored glass in Kitab al-Durra al-Maknuna (The Book of the Hidden Pearl), in addition to 12 recipes inserted by al-Marrakishi in a later edition of the book.[36] By the 11th century, clear glass mirrors were being produced in Islamic Spain.[citation needed]

Africa

[

edit

]

During post-classical times, glass and glass beads were also produced in the kingdom of Benin.[37]

Medieval Europe

[

edit

]

A 16th-century stained glass window

After the collapse of the Western Roman Empire, independent glass making technologies emerged in Northern Europe, with artisan forest glass produced by several cultures. Byzantine Glass evolved the Roman tradition, in the Eastern Empire. The claw beaker was popular as a relatively easy to make but an impressive vessel that exploited the unique potential of glass.[citation needed]

Glass objects from the 7th and 8th centuries have been found on the island of Torcello near Venice. These form an important link between Roman times and the later importance of that city in the production of the material. Around 1000 AD, an important technical breakthrough was made in Northern Europe when soda glass, produced from white pebbles and burnt vegetation was replaced by glass made from a much more readily available material: potash obtained from wood ashes. From this point on, northern glass differed significantly from that made in the Mediterranean area, where soda remained in common use.[38]

Until the 12th century, stained glass – glass to which metallic or other impurities had been added for coloring – was not widely used, but it rapidly became an important medium for Romanesque art and especially Gothic art. Almost all survivals are in church buildings, but it was also used in grand secular buildings. The 11th century saw the emergence in Germany of new ways of making sheet glass by blowing spheres. The spheres were swung out to form cylinders and then cut while still hot, after which the sheets were flattened. This technique was perfected in 13th century Venice. The crown glass process was used up to the mid-19th century. In this process, the glassblower would spin approximately 9 pounds (4 kg) of molten glass at the end of a rod until it flattened into a disk approximately 5 feet (1.5 m) in diameter. The disk would then be cut into panes. Domestic glass vessels in late medieval Northern Europe are known as forest glass.[citation needed]

Anglo-Saxon world

[

edit

]

Anglo-Saxon glass has been found across England during archaeological excavations of both settlement and cemetery sites. Glass in the Anglo-Saxon period was used in the manufacture of a range of objects including vessels, beads, windows and was even used in jewelry.[39] In the 5th century AD with the Roman departure from Britain, there were also considerable changes in the usage of glass.[40] Excavation of Romano-British sites has revealed plentiful amounts of glass but, in contrast, the amount recovered from the 5th century and later Anglo-Saxon sites is minuscule.[40]

The majority of complete vessels and assemblages of beads come from the excavations of early Anglo-Saxon cemeteries, but a change in burial rites in the late 7th century affected the recovery of glass, as Christian Anglo-Saxons were buried with fewer grave goods, and glass is rarely found. From the late 7th century onwards, window glass is found more frequently. This is directly related to the introduction of Christianity and the construction of churches and monasteries.[40][41] There are a few Anglo-Saxon ecclesiastical[42] literary sources that mention the production and use of glass, although these relate to window glass used in ecclesiastical buildings.[40][41][43] Glass was also used by the Anglo-Saxons in their jewelry, both as enamel or as cut glass insets.[44][45]

Murano

[

edit

]

The center for luxury Italian glassmaking from the 14th century was the island of Murano, which developed many new techniques and became the center of a lucrative export trade in dinnerware, mirrors, and other items. What made Venetian Murano glass significantly different was that the local quartz pebbles were almost pure silica, and were ground into a fine clear sand that was combined with soda ash obtained from the Levant, for which the Venetians held the sole monopoly. The clearest and finest glass is tinted in two ways: firstly, a natural coloring agent is ground and melted with the glass. Many of these coloring agents still exist today; for a list of coloring agents, see below. Black glass was called obsidianus after obsidian stone. A second method is apparently to produce a black glass which, when held to the light, will show the true color that this glass will give to another glass when used as a dye.[46]

The Venetian ability to produce this superior form of glass resulted in a trade advantage over other glass producing lands. Murano’s reputation as a center for glassmaking was born when the Venetian Republic, fearing fire might burn down the city’s mostly wood buildings, ordered glassmakers to move their foundries to Murano in 1291.[citation needed] Murano's glassmakers were soon the island’s most prominent citizens. Glassmakers were not allowed to leave the Republic. Many took a risk and set up glass furnaces in surrounding cities and as far afield as England and the Netherlands.[citation needed]

Bohemia

[

edit

]

Bohemian flashed and engraved ruby glass (19th-century)

Bohemian glass, or Bohemia crystal, is a decorative glass produced in regions of Bohemia and Silesia, now in the current state of the Czech Republic, since the 13th century.[47] Oldest archaeology excavations of glass-making sites date to around 1250 and are located in the Lusatian Mountains of Northern Bohemia. Most notable sites of glass-making throughout the ages are Skalice (German: Langenau), Kamenický Šenov (German: Steinschönau) and Nový Bor (German: Haida). Both Nový Bor and Kamenický Šenov have their own Glass Museums with many items dating since around 1600. It was especially outstanding in its manufacture of glass in high Baroque style from 1685 to 1750. In the 17th century, Caspar Lehmann, gem cutter to Emperor Rudolf II in Prague, adapted to glass the technique of gem engraving with copper and bronze wheels.[citation needed]

Modern glass production

[

edit

]

New processes

[

edit

]

Glassblowers at work. Retort making.

A very important advance in glass manufacture was the technique of adding lead oxide to the molten glass; this improved the appearance of the glass and made it easier to melt using sea-coal as a furnace fuel. This technique also increased the "working period" of the glass, making it easier to manipulate. The process was first discovered by George Ravenscroft in 1674, who was the first to produce clear lead crystal glassware on an industrial scale. Ravenscroft had the cultural and financial resources necessary to revolutionise the glass trade, allowing England to overtake Venice as the centre of the glass industry in the eighteenth and nineteenth centuries. Seeking to find an alternative to Venetian cristallo, he used flint as a silica source, but his glasses tended to crizzle, developing a network of small cracks destroying its transparency. This was eventually overcome by replacing some of the potash flux with lead oxide to the melt.[48]

He was granted a protective patent in where production and refinement moved from his glasshouse on the Savoy to the seclusion of Henley-on-Thames.[49]

By 1696, after the patent expired, twenty-seven glasshouses in England were producing flint glass and were exporting all over Europe with such success that, in 1746, the British Government imposed a lucrative tax on it. Rather than drastically reduce the lead content of their glass, manufacturers responded by creating highly decorated, smaller, more delicate forms, often with hollow stems, known to collectors today as Excise glasses.[50] The British glass making industry was able to take off with the repeal of the tax in 1845.

Evidence of the use of the blown plate glass method dates back to 1620 in London and was used for mirrors and coach plates. Louis Lucas de Nehou and A. Thevart perfected the process of casting Polished plate glass in 1688 in France. Prior to this invention, mirror plates, made from blown "sheet" glass, had been limited in size. De Nehou's process of rolling molten glass poured on an iron table rendered the manufacture of very large plates possible.[51] This method of production was adopted by the English in 1773 at Ravenhead. The polishing process was industrialized around 1800 with the adoption of a steam engine to carry out the grinding and polishing of the cast glass.

Industrial production

[

edit

]

The façade of the Crystal Palace, one of the first buildings to use glass as the main material for construction.

The use of glass as a building material was heralded by The Crystal Palace of 1851, built by Joseph Paxton to house the Great Exhibition. Paxton's revolutionary new building inspired the public use of glass as a material for domestic and horticultural architecture. In 1832, the British Crown Glass Company (later Chance Brothers) became the first company to adopt the cylinder method to produce sheet glass with the expertise of Georges Bontemps, a famous French glassmaker.[n 4] This glass was produced by blowing long cylinders of glass, which were then cut along the length and then flattened onto a cast-iron table, before being annealed. Plate glass involves the glass being ladled onto a cast-iron bed, where it is rolled into a sheet with an iron roller. The sheet, still soft, is pushed into the open mouth of an annealing tunnel or temperature-controlled oven called a lehr, down which it was carried by a system of rollers.[52] James Hartley introduced the Rolled Plate method in 1847. This allowed a ribbed finish and was often used for extensive glass roofs such as within railway stations.

An early advance in automating glass manufacturing was patented in 1848 by the engineer Henry Bessemer. His system produced a continuous ribbon of flat glass by forming the ribbon between rollers. This was an expensive process, as the surfaces of the glass needed polishing and was later abandoned by its sponsor, Robert Lucas Chance of Chance Brothers, as unviable. Bessemer also introduced an early form of "Float Glass" in 1843, which involved pouring glass onto liquid tin.

In 1887, the mass production of glass was developed by the firm Ashley in Castleford, Yorkshire. This semi-automatic process used machines that were capable of producing 200 standardized bottles per hour, many times quicker than the traditional methods of manufacture.[53] Chance Brothers also introduced the machine rolled patterned glass method in 1888.[54]

In 1898, Pilkington invented Wired Cast glass, where the glass incorporates a strong steel-wire mesh for safety and security. This was commonly given the misnomer "Georgian Wired Glass" but it greatly post-dates the Georgian era.[55] The Machine Drawn Cylinder technique was invented in the US and was the first mechanical method for the drawing of window glass. It was manufactured under licence in the UK by Pilkington from 1910 onwards.

In 1938, the polished plate process was improved by Pilkington which incorporated a double grinding process to give an improved quality to the finish. Between 1953 and 1957, Sir Alastair Pilkington and Kenneth Bickerstaff of the UK's Pilkington Brothers developed the revolutionary float glass process, the first successful commercial application for forming a continuous ribbon of glass using a molten tin bath on which the molten glass flows unhindered under the influence of gravity.[56] This method gave the sheet uniform thickness and very flat surfaces. Modern windows are made from float glass. Most float glass is soda–lime glass, but relatively minor quantities of specialty borosilicate[57] and flat panel display glass are also produced using the float glass process. The success of this process lay in the careful balance of the volume of glass fed onto the bath, where it was flattened by its own weight.[58] Full scale profitable sales of float glass were first achieved in 1960.

[

edit

]

See also

[

edit

]

Notes

[

edit

]

  1. a b

    True glazing over a ceramic body was not used until many centuries after the production of the first glass.

  2. ^[10]

    Found on the MY Oi 701, MY Oi 702, MY Oi 703 and MY Oi 704 tablets; the least damaged, as far as this word is concerned, is MY Oi 703.

  3. ^Cf.

    κύανος

    .[11]
  4. ^

    This process was used extensively until early in the 20th Century to make window glass.

References

[

edit

]

Further reading

[

edit

]

20. BLOB - Also called a blob-top, blob collar, beer finish, rounded collarrounded taper, donut or donut ring (if relatively narrow), single rounded collar, soda finish, spherical finish, and possibly other names though it is not clear what glass manufacturers actually called this finish. Click http://www.sha.org/bottle/pdffiles/IMACSfinishes.pdf to see the illustration (#20) in the IMACS table.

This one-part finish looks like its name in that it is a distinctly outwardly rounded and tooled "blob" of glass that can be uniform and vertically symmetrical or vertically asymmetrical like the examples pictured here (covered more later).  This style of one-part finish is found in many subtle variations as to form and size, only some of which are pictured here.  The blob finish can sometimes grade into and look similar to the oil (#11) and packer finishes (#8) - both of which have a much less distinctly rounded outside surface - and sometimes approach the dimensions of the bead finish (#3), though the bead is much narrower vertically.  Compare the photos of each of these finishes to see the variably subtle differences.

As far as can be determined today, the term blob was never used by glass manufacturers for this broad category of single part finishes.  It is instead a modern, collector based term for a category of one-part finishes which share the general features described above.  Early bottle maker catalogs usually referred to the type of closure (e.g., Hutchinson, cork, Baltimore seal) instead of the blob finish itself on bottle types that this finish was common on (Illinois Glass Co. 1903, 1908, 1911).  Because of the wide variation in blob finishes there are many recognizable sub-forms that could be assigned different names and may have some dating relevance.  For example, there are blob finishes which are wider towards the rim than the base of the finish ("top-weighted" like the two pictures to the below left), blobs that are wider towards the bottom than the top ("bottom-weighted" like the pictures above and below right), and ones that are symmetrical with the widest part in the middle ("balanced" blobs).  (The task of splitting out variations will be deferred to future revisions of this website.)

To the right is an illustration from an 1876 patent which shows a typical calipers type finishing tool used to create a type of applied, one-part "blob" finish used for carbonated beverages.  (Click J. Lamont's May 29, 1876 Patent #183,267 to see the entire patent.)  The blob finish and upper neck of the bottle is visible being held between within the "jaws" of the calipers type finishing tool which is otherwise quite typical of the tools used to finish bottles from at least the 1840s until the end of the mouth-blown bottle era.

Blob finishes are most commonly found on soda and mineral water bottles from the 184s through the end of the mouth-blown era (1920 or so) and beer bottles from the 1870s into the 1910s.  This style was occasionally but not commonly used on other types of bottles including patent or proprietary medicines and even a few figured flasks dating from the mid-19th century.  McKearin & Wilson (1978) called this finish a "tooled, rounded rolled-over collar" on figured flasks.  The wide period of use precludes any general dating conclusions simply based on the shape; other diagnostic features must be used, including the bottle type itself.  See the Bottle Typing page for more information.

The tooled "funnel" shaped blob finish to the left is on a Mt. Hood Soda Water (Portland, OR.) that dates from around 1906-1911 (Fowler 1981,1998; Elliot & Gould 1988).  The base of this bottle has an three digit mold mark (362 / H) which was thought to be a makers mark for the Holt Glass Works, which was allegedly destroyed by the April 18th, 1906 San Francisco earthquake (Toulouse 1971; Thomas 1998).   However, that has since been found incorrect as the company expired in the 1890s long before that famous event.  See the following link on this site for more information on Holt:  https://sha.org/bottle/pdffiles/Holt.pdf   This bottle also still has the wire Hutchinson closure in place - see Part III - Types of Bottle Closures for more information.

(Note:  There is possibly some dating refinement to be had related to the subtly varying conformation of blob finishes on Hutchinson sodas - at least in the Western US.  For more information, consult Elliott & Gould's 1988 book entitled "Hawaiian Bottles of Long Ago" for more on this subject.  Although developed for Hawaiian Hutchinson soda bottles, it has application elsewhere since all Hutchinson soda bottles used in Hawaii were imported, and largely from the U.S. mainland.  As an example of this dating potential,  the aqua blob finish pictured above (Mt. Hood Soda Water) was classified by Elliott & Gould as a "funnel top" since the finish itself is somewhat funnel like in its taper from top to bottom.  They note that this style was used on bottles known to be dating from 1905 into the early 1910s - a date rage that fits with noted the company history.  Those authors believe that the funnel finish was introduced and used by the Pacific Coast Glass Company (California) - a likely producer of this Oregon soda.)

The applied blob finish in the upper left corner (blue-green bottle) is on an early soda/mineral water bottle embossed The Excelsior Water (possibly from San Francisco, CA.) that was most likely made in 1850s based on the improved pontil mark on the base (Markota 1994).  This style of finish on this shape of bottle (a "blob soda" shape, though most made had round bodies instead of 8-sided) was very common and these bottles were made in a wide variety of colors for use throughout the United States primarily between 1850 and about 1885.  The "blob soda" style was, however, made as early as the 1840s and as late as the early 20th century (McKearin & Wilson 1978; Illinois Glass Co. 1908, 1911).

The tooled amber blob finish to the right above is on a Buffalo Brewing Company bottle (Sacramento, CA.) that dates between 1890 and 1902.  How do we know this?  The Buffalo Brewing Company began business in 1889 with the first production in May of 1890, setting the oldest possible date for the bottle as 1890 (Groff 2002).  In addition, the base is embossed with the makers mark S.F.& P.G.W.  which stands for the San Francisco & Pacific Glass Works.  This glass company was merged out of existence in 1902 (Toulouse 1971).  Viola!  A date range of 1890 to 1902.  Physical diagnostic confirmation of this date range - and maybe even a narrowing down to the mid 1890s to 1902 - is supported by the tooled finish and evidence of mold air venting - three small dots on both the front and back shoulders.  This bottle also has the Lightening closure still in place though the rubber seal is long gone - see Part III - Types of Bottle Closures for more information.

The amber applied blob finish to the left is on a Warner's Safe Kidney & Liver Cure (Rochester, NY) that likely dates between 1885 and 1890 based on company history and diagnostic features (Wilson & Wilson 1971, Seeliger 1974).  Though commonly found on Warner's medicinal products, blob finishes on medicinal bottles was not typical but did occur with enough frequency that one should be aware of it.

Also see Tod von Mechow's exceptional website on early soda, mineral water and beer bottles at the following link for more information on specific diagnostic features of these type bottles - including the use of this finish type (which he terms a "rounded taper") - which can help refine the dating:  http://www.sodasandbeers.com  In particular, see his page on beer finish types - http://www.sodasandbeers.com/SABBottleLipsBeer.htm - and soda/mineral water finish types - http://www.sodasandbeers.com/SABBottleLipsSoda.htm .  These pages help refine what this author has lumped together as simply "blob" finishes.